Development of epoxy resin has been committed to high-quality, has made a number of achievements in scientific research. Development of a series of popular paint products, has been applied in the field of high strength concrete, road repair, waterproof plugging, cement basecomposite pavement, sealing, anti-corrosion coatings, adhesives and other.
Company culture: the company to "focus on resin, intentions services" as the core value, all the user needs, hopes to professional standards and unremitting efforts, good image enterprise, provides the service guidance for the enterprise product promotion of cultural development.
Company main products: mainly coatings, adhesives, constructionenterprises to provide sophisticated quality of waterborne epoxy resin and curing agent for epoxy resin.
Vision: to be the best Chinese waterborne epoxy resin enterprises.
Company commitment: the development of waterborne epoxy resin withthe newer and better.
Anticorrosive primer performance test: impact resistance of >100cmgrade<1; adhesion; salt (10%NaCl) >7 days, the film;
Resistance to acid and alkali (10%NaOH10%HCL) >4 days, the film is good
Anticorrosive paint performance test: impact resistance of >80cm grade<1; adhesion; salt (10%NaCl) >7 days, the film;
Resistance to acid and alkali (10%NaOH10%HCL) >5 days, the film is good
Varnish performance test: the construction period (25 ℃) ≤ 1.5h; impact resistance of >100cm adhesion to<0 level;
Salt water (10%NaCl) >7 days, good acid and alkali resistance of paint film; (10%NaOH10%HCL) >4 days, the film is good
Waterborne epoxy mortar modified asphalt pavement and the asphalt pavement performance comparison:
The splitting tensile strength of /Mpa compressive modulus /MPatechnical index of compressive strength of /Mpa
7d (25 ℃) resin modified road 2.54 1.441216
14d (25 ℃) resin modified road 3.17 1.611841
28d (25 ℃) ordinary asphalt pavement 2.90 1.071396
28d (25 ℃) resin modified road 3.79 1.852247